戊烷二肼

反应条件: temp:75.01; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: In the dropping tank of a reaction vessel (tank) equipped with a stirrer, a thermometer, a nitrogen-sealing tube, a condenser and a dropping tank were placed 8.0 parts of MMA, 15.0 parts of BA, 1.0 part of AA, 1.0 part of 2-ethylhexyl acrylate (referred to here-inafter as EHA), 10.0 parts of acrylonitrile (referred to hereinafter as AN), 5.0 parts of HEMA, 5.0 parts of DAAA, 1.0 part of AIBN, 25 parts of MEK and 25 parts of IPA and then uniformly mixed. Separately, in the reaction tank were placed 20.0 parts of PA-8, 8.0 parts of MMA, 15.0 parts of BA, 1.0 part of AA, 1.0 part of EHA, 10.0 parts of AN, 5.0 parts of HEMA, 5.0 parts of DAAA, 20 parts of MEK and 20 parts of IPA and then uniformly mixed. Subsequently, the reaction tank was heated to 75° C. and the liquid mixture in the dropping tank was dropped into the reaction tank over 5 hours. Thereafter, the resulting mixture was further subjected to reaction at the same temperature for 4 hours. Thereafter, 2.8 parts of TEA was added to the reaction mixture to sufficiently neutralize the same and then aqueous hydrazide consisting of 148 parts of distilled water and 4.7 parts of glutaric acid dihydrazide (referred to hereinafter as GDH) was added thereto to emulsify the reaction mixture. Thereafter, the MEK and the IPA present in the system were removed at 60° C. at 100 Torr to obtain an aqueous emulsion of a self-emulsifiable acryl-urethane copolymer having a solid content of 39.9% (the emulsion is referred to hereinafter as EA-11). In the dropping tank of a reaction vessel (tank) equipped with a stirrer uniformly mixed uniformly mixed the liquid mixture in the dropping tank was dropped into the reaction tank over 5 hours Thereafter, the resulting mixture was further subjected to reaction at the same temperature for 4 hours Thereafter, 2.8 parts of TEA was added to the reaction mixture was added Thereafter, the MEK and the IPA present in the system were removed at 60° C. at 100 Torr

反应条件: temp:75.01; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: In the dropping tank of a reaction vessel (tank) equipped with a stirrer, a thermometer, a nitrogen-sealing tube, a condenser and a dropping tank were placed 8.0 parts of MMA, 15.0 parts of BA, 1.0 part of AA, 1.0 part of 2-ethylhexyl acrylate (referred to here-inafter as EHA), 10.0 parts of acrylonitrile (referred to hereinafter as AN), 5.0 parts of HEMA, 5.0 parts of DAAA, 1.0 part of AIBN, 25 parts of MEK and 25 parts of IPA and then uniformly mixed. Separately, in the reaction tank were placed 20.0 parts of PA-8, 8.0 parts of MMA, 15.0 parts of BA, 1.0 part of AA, 1.0 part of EHA, 10.0 parts of AN, 5.0 parts of HEMA, 5.0 parts of DAAA, 20 parts of MEK and 20 parts of IPA and then uniformly mixed. Subsequently, the reaction tank was heated to 75° C. and the liquid mixture in the dropping tank was dropped into the reaction tank over 5 hours. Thereafter, the resulting mixture was further subjected to reaction at the same temperature for 4 hours. Thereafter, 2.8 parts of TEA was added to the reaction mixture to sufficiently neutralize the same and then aqueous hydrazide consisting of 148 parts of distilled water and 4.7 parts of glutaric acid dihydrazide (referred to hereinafter as GDH) was added thereto to emulsify the reaction mixture. Thereafter, the MEK and the IPA present in the system were removed at 60° C. at 100 Torr to obtain an aqueous emulsion of a self-emulsifiable acryl-urethane copolymer having a solid content of 39.9% (the emulsion is referred to hereinafter as EA-11). In the dropping tank of a reaction vessel (tank) equipped with a stirrer uniformly mixed uniformly mixed the liquid mixture in the dropping tank was dropped into the reaction tank over 5 hours Thereafter, the resulting mixture was further subjected to reaction at the same temperature for 4 hours Thereafter, 2.8 parts of TEA was added to the reaction mixture was added Thereafter, the MEK and the IPA present in the system were removed at 60° C. at 100 Torr

反应条件: temp:75.01; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: In the dropping tank of a reaction vessel (tank) equipped with a stirrer, a thermometer, a nitrogen-sealing tube, a condenser and a dropping tank were placed 8.0 parts of MMA, 15.0 parts of BA, 1.0 part of AA, 1.0 part of 2-ethylhexyl acrylate (referred to here-inafter as EHA), 10.0 parts of acrylonitrile (referred to hereinafter as AN), 5.0 parts of HEMA, 5.0 parts of DAAA, 1.0 part of AIBN, 25 parts of MEK and 25 parts of IPA and then uniformly mixed. Separately, in the reaction tank were placed 20.0 parts of PA-8, 8.0 parts of MMA, 15.0 parts of BA, 1.0 part of AA, 1.0 part of EHA, 10.0 parts of AN, 5.0 parts of HEMA, 5.0 parts of DAAA, 20 parts of MEK and 20 parts of IPA and then uniformly mixed. Subsequently, the reaction tank was heated to 75° C. and the liquid mixture in the dropping tank was dropped into the reaction tank over 5 hours. Thereafter, the resulting mixture was further subjected to reaction at the same temperature for 4 hours. Thereafter, 2.8 parts of TEA was added to the reaction mixture to sufficiently neutralize the same and then aqueous hydrazide consisting of 148 parts of distilled water and 4.7 parts of glutaric acid dihydrazide (referred to hereinafter as GDH) was added thereto to emulsify the reaction mixture. Thereafter, the MEK and the IPA present in the system were removed at 60° C. at 100 Torr to obtain an aqueous emulsion of a self-emulsifiable acryl-urethane copolymer having a solid content of 39.9% (the emulsion is referred to hereinafter as EA-11). In the dropping tank of a reaction vessel (tank) equipped with a stirrer uniformly mixed uniformly mixed the liquid mixture in the dropping tank was dropped into the reaction tank over 5 hours Thereafter, the resulting mixture was further subjected to reaction at the same temperature for 4 hours Thereafter, 2.8 parts of TEA was added to the reaction mixture was added Thereafter, the MEK and the IPA present in the system were removed at 60° C. at 100 Torr

反应条件: temp:75.01; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: In the dropping tank of a reaction vessel (tank) equipped with a stirrer, a thermometer, a nitrogen-sealing tube, a condenser and a dropping tank were placed 8.0 parts of MMA, 15.0 parts of BA, 1.0 part of AA, 1.0 part of 2-ethylhexyl acrylate (referred to here-inafter as EHA), 10.0 parts of acrylonitrile (referred to hereinafter as AN), 5.0 parts of HEMA, 5.0 parts of DAAA, 1.0 part of AIBN, 25 parts of MEK and 25 parts of IPA and then uniformly mixed. Separately, in the reaction tank were placed 20.0 parts of PA-8, 8.0 parts of MMA, 15.0 parts of BA, 1.0 part of AA, 1.0 part of EHA, 10.0 parts of AN, 5.0 parts of HEMA, 5.0 parts of DAAA, 20 parts of MEK and 20 parts of IPA and then uniformly mixed. Subsequently, the reaction tank was heated to 75° C. and the liquid mixture in the dropping tank was dropped into the reaction tank over 5 hours. Thereafter, the resulting mixture was further subjected to reaction at the same temperature for 4 hours. Thereafter, 2.8 parts of TEA was added to the reaction mixture to sufficiently neutralize the same and then aqueous hydrazide consisting of 148 parts of distilled water and 4.7 parts of glutaric acid dihydrazide (referred to hereinafter as GDH) was added thereto to emulsify the reaction mixture. Thereafter, the MEK and the IPA present in the system were removed at 60° C. at 100 Torr to obtain an aqueous emulsion of a self-emulsifiable acryl-urethane copolymer having a solid content of 39.9% (the emulsion is referred to hereinafter as EA-11). In the dropping tank of a reaction vessel (tank) equipped with a stirrer uniformly mixed uniformly mixed the liquid mixture in the dropping tank was dropped into the reaction tank over 5 hours Thereafter, the resulting mixture was further subjected to reaction at the same temperature for 4 hours Thereafter, 2.8 parts of TEA was added to the reaction mixture was added Thereafter, the MEK and the IPA present in the system were removed at 60° C. at 100 Torr