反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: 2,-4-diethylthioxanthone 2-ethylanthraquinone; 2-methylanthraquinone; 1,8-dihydroxyanthraquinone; dibenzoylperoxide; 2,2-dimethoxy-2-phenylacetophenone; benzoin; 2-hydroxy-2-methylpropiophenone; benzaldehyde; 4-(2-hydroxyethoxy)phenyl-(2-hydroxy-2-methylpropyl)-ketone; benzoylacetone;

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: Examples of commercially available radical photopolymerization initiator include IRGACURE 651 (2,2-dimethoxy-1,2-diphenyl ethane-1-on), IRGACURE 184 (1-hydroxycyclohexyl-phenyl-ketone), DAROCUR 1173 (2-hydroxy-2-methyl-1-phenyl-propane-1-on), IRGACURE 2959 (1-[4-(2-hydroxyethoxy)-phenyl]-2-hydroxy-2-methyl-1-propane-1-on), IRGACURE 127 (2-hydroxy-1-{4-[4-(2-hydroxy-2-methyl-propnyl)-benzyl]phenyl}-2-methyl-propane-1-on, IRGACURE 907 (2-methyl-1-(4-methyl thiophenyl)-2-morpholinopropane-1-on), IRGACURE 369 (2-benzyl-2-dimethylamino-1-(4-morpholinophenyl)-butanone-1), IRGACURE 379 (2-(dimethylamino)-2-[(4-methylphenyl)methyl]-1-[4-(4-morpholinyl)phenyl]-1-butanone), DAROCUR TPO (2,4,6-trimethylbenzoyl-diphenyl-phosphine oxide), IRGACURE 819 (bis(2,4,6-trimethylbenzoyl)-phenyl phosphine oxide), IRGACURE 784 (bis(eta-5-2,4-cyclopentadiene-1-yl)-bis(2,6-difluoro-3-(1H-pyrrole-1-yl)-phenyl)titanium), IRGACURE OXE 01 (1.2-octanedione, 1-[4-(phenylthio)-, 2-(o-benzoyloxime)]), IRGACURE OXE 02 (ethanone, 1-[9-ethyl-6-(2-methylbenzoyl)-9H-carbazole-3-yl]-, 1-(o-acetyloxime)), and IRGACURE 754 (mixture of oxyphenyl acetic acid, 2-[2-oxo-2-phenylacetoxyethoxy]ethyl ester and oxyphenyl acetic acid, 2-(2-hydroxyethoxy)ethyl ester)(all produced by BASF); Speedcure TPO (produced by Lambson), KAYACURE DETX-S (2,4-diethylthioxantone) (produced by Nippon Kayaku Co., Ltd.); Lucirin TPO, LR8893, LR8970 (produced by BASF); Ubecryl P36 (produced by UCB), and the like. all produced by BASF)

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: 2-methyl-1-[4-(methyl thio)-phenyl]-2-morpholinopropanone-1; 1-(4-isopropylphenyl)-2-hydroxy-2-methylpropan-1-one; 1-(4-dodecyl-phenyl)-2-hydroxy-2-methylpropan-1-one; 4-(2-hydroxyethoxy)phenyl-2(2-hydroxy-2-propyl)-ketone; diethoxyphenyl acetophenone; 2,4,6 trimethylbenzoyl diphenylphosphone, a mixture of (2,6-dimethoxy benzoyl)-2,4,4 trimethylpentylphosphineoxide and 2-hydroxy-2-methyl-1-phenyl-propane-1-one, and mixtures thereof.

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: 2-methyl-1-[4-(methyl thio)-phenyl]-2-morpholinopropanone-1; 1-(4-isopropylphenyl)-2-hydroxy-2-methylpropan-1-one; 1-(4-dodecyl-phenyl)-2-hydroxy-2-methylpropan-1-one; 4-(2-hydroxyethoxy)phenyl-2(2-hydroxy-2-propyl)-ketone; diethoxyphenyl acetophenone; 2,4,6 trimethylbenzoyl diphenylphosphone, a mixture of (2,6-dimethoxy benzoyl)-2,4,4 trimethylpentylphosphineoxide and 2-hydroxy-2-methyl-1-phenyl-propane-1-one, and mixtures thereof.

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: A 250 mL three-neck round bottom flask was charged with toluene (81 mL) and cooled to <−50° C. with a dry ice/acetone bath. 3,3,3-Trifluoropropene (10.28 g, 107.0 mmol) was bubbled into the solvent and the ice bath was removed. 3-Mercaptopropionic acid (9.200 g, 86.70 mmol) and 2,2-dimethoxy-2-phenylacetophenone (1.070 g, 4.170 mmol) was added and the long wave light (366 nm, 4 watt UVP lamp) was turned on (Starting temperature: −24° C.). The reaction reached a temperature of 27.5° C. due to heat from the lamp. The reaction was stirred with the black light on for 4 hours. After 4 hours the black light was turned off and the reaction concentrated by rotary evaporation (41° C., 6 mm Hg) giving a pale yellow oil (18.09 g, 51:1 linear:branched isomer, 90 wt % linear isomer by GC internal standard assay, 16.26 g active, 93%). The crude material was dissolved in 10% sodium hydroxide w/w (37.35 g) and was washed with toluene (30 mL) to remove non-polar impurities. The aqueous layer was acidified to pH ˜2-3 with hydrochloric acid (2 N, 47.81 g) and was extracted with toluene (50 mL). The organic layer was washed with water (40 mL) and dried over magnesium sulfate, filtered, and concentrated by rotary evaporation giving a pale yellow oil (14.15 g, 34:1 linear:branched isomer, 94 wt % linear isomer by GC internal standard assay, 13.26 g active, 76%): 1H NMR (400 MHz, CDCl3) δ 2.83 (td, J=7.1, 0.9 Hz, 2H), 2.76-2.64 (m, 4H), 2.47-2.30 (m, 2H); 13C NMR (101 MHz, CDCl3) δ 177.68, 125.91 (q, J=277.1 Hz), 34.58 (q, J=28.8 Hz), 34.39, 26.63, 24.09 (q, J=3.3 Hz); 19F NMR (376 MHz, CDCl3) δ −66.49. cooled to <−50° C. with a dry ice/acetone bath the ice bath was removed was turned on (Starting temperature: −24° C.) a temperature of 27.5° C. to heat from the lamp After 4 hours the black light was turned off the reaction concentrated by rotary evaporation (41° C., 6 mm Hg) giving a pale yellow oil (18.09 g, 51:1 linear:branched isomer, 90 wt % linear isomer by GC internal standard assay, 16.26 g active, 93%) was washed with toluene (30 mL) to remove non-polar impurities was extracted with toluene (50 mL) The organic layer was washed with water (40 mL) dried over magnesium sulfate filtered concentrated by rotary evaporation giving a pale yellow oil (14.15 g, 34:1 linear:branched isomer, 94 wt % linear isomer by GC internal standard assay, 13.26 g active, 76%)

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: A 500 mL three-neck round bottomed flask was charged with toluene (200 mL) and cooled to <−50° C. with a dry ice/acetone bath. 3,3,3-Trifluoropropene (21.8 g, 227 mmol) was condensed into the reaction by bubbling the gas through the cooled solvent and the ice bath was removed. Methyl 3-mercaptopropionate (26.8 g, 223 mmol) and 2,2-dimethoxy-2-phenylacetophenone (2.72 g, 10.61 mmol) were added and a UVP lamp (4 watt) that was placed within 2 centimeters of the glass wall was turned on to the long wave function (366 nanometers). The reaction reached 35° C. due to heat from the lamp. After 4 hours, all of the trifluoropropene was either consumed or boiled out of the reaction. The light was turned off and the reaction stirred at room temperature overnight. After 22 hours, more trifluoropropene (3.1 g) was bubbled through the mixture at room temperature and the light was turned on for an additional 2 hours. The reaction had reached 93% conversion, so no more trifluoropropene was added. The light was turned off and the mixture concentrated on the rotovap (40° C., 20 torr) giving a yellow liquid (45.7 g, 21.3:1 linear:branched isomer, 75 wt % pure linear isomer determined by a GC internal standard assay, 34.3 g active, 71% in pot yield). cooled to <−50° C. with a dry ice/acetone bath condensed into the reaction by bubbling the gas through the cooled solvent the ice bath was removed a UVP lamp (4 watt) that was placed within 2 centimeters of the glass wall reached 35° C. to heat from the lamp either consumed boiled out of the reaction After 22 hours more trifluoropropene (3.1 g) was bubbled through the mixture at room temperature was turned on for an additional 2 hours so no more trifluoropropene was added the mixture concentrated on the rotovap (40° C., 20 torr) giving a yellow liquid (45.7 g, 21.3:1 linear 71% in pot yield)

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: A 250 mL three-neck round bottomed flask was charged with toluene (81 mL) and cooled to <−50° C. with a dry ice/acetone bath. 3,3,3-Trifluoropropene (10.28 g, 107.0 mmol) was bubbled into the solvent and the ice bath was removed. 3-Mercaptopropionic acid (9.200 g, 86.70 mmol) and 2,2-dimethoxy-2-phenylacetophenone (1.070 g, 4.170 mmol) was added and the long wave light (366 nm, 4 watt UVP lamp) was turned on (Starting temperature: −24° C.). The reaction reached a temperature of 27.5° C. due to heat from the lamp. The reaction was stirred with the black light on for 4 hours. After 4 hours the black light was turned off and the reaction concentrated by rotary evaporation (41° C., 6 mm Hg) giving a pale yellow oil (18.09 g, 51:1 linear:branched isomer, 90 wt % linear isomer by GC internal standard assay, 16.26 g active, 93%). The crude material was dissolved in 10% sodium hydroxide w/w (37.35 g) and was washed with toluene (30 mL) to remove non-polar impurities. The aqueous layer was acidified to pH ˜2-3 with hydrochloric acid (2 N, 47.81 g) and was extracted with toluene (50 mL). The organic layer was washed with water (40 mL) and dried over magnesium sulfate, filtered, and concentrated by rotary evaporation giving a pale yellow oil (14.15 g, 34:1 linear:branched isomer, 94 wt % linear isomer by GC internal standard assay, 13.26 g active, 76%). cooled to <−50° C. with a dry ice/acetone bath the ice bath was removed was turned on (Starting temperature: −24° C.) a temperature of 27.5° C. to heat from the lamp After 4 hours the black light was turned off the reaction concentrated by rotary evaporation (41° C., 6 mm Hg) giving a pale yellow oil (18.09 g, 51:1 linear:branched isomer, 90 wt % linear isomer by GC internal standard assay, 16.26 g active, 93%) was washed with toluene (30 mL) to remove non-polar impurities was extracted with toluene (50 mL) The organic layer was washed with water (40 mL) dried over magnesium sulfate filtered concentrated by rotary evaporation giving a pale yellow oil (14.15 g, 34:1 linear:branched isomer, 94 wt % linear isomer by GC internal standard assay, 13.26 g active, 76%)

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: The acrylic monomers generated in Examples 1 and 10-12, 2-OA, 2-EHA, and LA were each prepared into adhesive films using the following procedure. The alkyl acrylate (28.5 g), 0.02 g of IRGACURE 651 (Ciba), 0.3 g of acrylic acid (AA, Alfa Aesar), and 1.2 g of hydroxyethyl acrylate (HEA, Aldrich) were mixed using a magnetic stir bar in a clear glass vial. The glass vial was then purged with nitrogen for 5 minutes to remove dissolved oxygen, and then treated with UV light (365 nm, approximately 5 mW/cm2) until a coatable viscosity was achieved. The target for this step was an approximate viscosity of 3000 cP at room temperature and acrylic conversion of approximately 10%. each prepared into adhesive films The glass vial was then purged with nitrogen for 5 minutes to remove dissolved oxygen treated with UV light (365 nm, approximately 5 mW/cm2) until a coatable viscosity at room temperature

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: The acrylic monomers generated in Examples 1 and 10-12, 2-OA, 2-EHA, and LA were each prepared into adhesive films using the following procedure. The alkyl acrylate (28.5 g), 0.02 g of IRGACURE 651 (Ciba), 0.3 g of acrylic acid (AA, Alfa Aesar), and 1.2 g of hydroxyethyl acrylate (HEA, Aldrich) were mixed using a magnetic stir bar in a clear glass vial. The glass vial was then purged with nitrogen for 5 minutes to remove dissolved oxygen, and then treated with UV light (365 nm, approximately 5 mW/cm2) until a coatable viscosity was achieved. The target for this step was an approximate viscosity of 3000 cP at room temperature and acrylic conversion of approximately 10%. each prepared into adhesive films The glass vial was then purged with nitrogen for 5 minutes to remove dissolved oxygen treated with UV light (365 nm, approximately 5 mW/cm2) until a coatable viscosity at room temperature

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: A 500 mL three-neck round bottom flask was charged with toluene (200 mL) and cooled to <−50° C. with a dry ice/acetone bath. 3,3,3-Trifluoropropene (21.8 g, 227 mmol) was condensed into the reaction by bubbling the gas through the cooled solvent and the ice bath was removed. Methyl 3-mercaptopropionate (26.8 g, 223 mmol) and 2,2-dimethoxy-2-phenylacetophenone (2.72 g, 10.61 mmol) were added and a UVP lamp (4 watt) that was placed within 2 centimeters of the glass wall was turned on to the long wave function (366 nanometers). The reaction reached 35° C. due to heat from the lamp. After 4 hours, all of the trifluoropropene was either consumed or boiled out of the reaction. The light was turned off and the reaction stirred at room temperature overnight. After 22 hours, more trifluoropropene (3.1 g) was bubbled through the mixture at room temperature and the light was turned on for an additional 2 hours. The reaction had converted 93% so no more trifluoropropene was added. The light was turned off and the mixture concentrated on the rotovap (40° C., 20 torr) giving a yellow liquid (45.7 g, 21.3:1 linear: branched isomer, 75 wt % pure linear isomer determined by a GC internal standard assay, 34.3 g active, 71% in pot yield). cooled to <−50° C. with a dry ice/acetone bath condensed into the reaction by bubbling the gas through the cooled solvent the ice bath was removed a UVP lamp (4 watt) that was placed within 2 centimeters of the glass wall reached 35° C. to heat from the lamp either consumed boiled out of the reaction After 22 hours more trifluoropropene (3.1 g) was bubbled through the mixture at room temperature was turned on for an additional 2 hours was added the mixture concentrated on the rotovap (40° C., 20 torr) giving a yellow liquid (45.7 g, 21.3:1 linear 71% in pot yield)

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: A 500 mL three-neck round bottom flask was charged with toluene (200 mL) and cooled to <−50° C. with a dry ice/acetone bath. 3,3,3-Trifluoropropene (21.8 g, 227 mmol) was condensed into the reaction by bubbling the gas through the cooled solvent and the ice bath was removed. Methyl 3-mercaptopropionate (26.8 g, 223 mmol) and 2,2-dimethoxy-2-phenylacetophenone (2.72 g, 10.61 mmol) were added and a UVP lamp (4 watt) that was placed within 2 centimeters of the glass wall was turned on to the long wave function (366 nanometers). The reaction reached 35° C. due to heat from the lamp. After 4 hours, all of the trifluoropropene was either consumed or boiled out of the reaction. The light was turned off and the reaction stirred at room temperature overnight. After 22 hours, more trifluoropropene (3.1 g) was bubbled through the mixture at room temperature and the light was turned on for an additional 2 hours. The reaction had converted 93% so no more trifluoropropene was added. The light was turned off and the mixture concentrated on the rotovap (40° C., 20 torr) giving a yellow liquid (45.7 g, 21.3:1 linear: branched isomer, 75 wt % pure linear isomer determined by a GC internal standard assay, 34.3 g active, 71% in pot yield). cooled to <−50° C. with a dry ice/acetone bath condensed into the reaction by bubbling the gas through the cooled solvent the ice bath was removed a UVP lamp (4 watt) that was placed within 2 centimeters of the glass wall reached 35° C. to heat from the lamp either consumed boiled out of the reaction After 22 hours more trifluoropropene (3.1 g) was bubbled through the mixture at room temperature was turned on for an additional 2 hours was added the mixture concentrated on the rotovap (40° C., 20 torr) giving a yellow liquid (45.7 g, 21.3:1 linear 71% in pot yield)

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: A 250 mL three-neck round bottom flask was charged with toluene (81 mL) and cooled to <−50° C. with a dry ice/acetone bath. 3,3,3-Trifluoropropene (10.28 g, 107.0 mmol) was bubbled into the solvent and the ice bath was removed. 3-Mercaptopropionic acid (9.200 g, 86.70 mmol) and 2,2-dimethoxy-2-phenylacetophenone (1.070 g, 4.170 mmol) were added and the long wave light (366 nm, 4 watt UVP lamp) was turned on (Starting temperature: −24° C.). The reaction reached a high temperature of 27.5° C. due to heat from the lamp. The reaction was stirred with the black light on for 4 hours. After 4 hours the black light was turned off and the reaction concentrated by rotary evaporation (41° C., 6 mm Hg) giving a pale yellow oil (18.09 g, 51:1 linear:branched isomer, 90 wt % linear isomer by GC internal standard assay, 16.26 g active, 93%). The crude material was dissolved in sodium hydroxide w/w (10%, 37.35 g) and was washed with toluene (30 mL) to remove non-polar impurities. The aqueous layer was acidified to pH ˜2-3 with hydrochloric acid (2 N, 47.81 g) and was extracted with toluene (50 mL). The organic layer was washed with water (40 mL) and dried over magnesium sulfate, filtered, and concentrated by rotary evaporation giving a pale yellow oil (14.15 g, 34:1 linear:branched isomer, 94 wt % linear isomer by GC internal standard assay, 13.26 g active, 76%). cooled to <−50° C. with a dry ice/acetone bath the ice bath was removed was turned on (Starting temperature: −24° C.) a high temperature of 27.5° C. to heat from the lamp After 4 hours the black light was turned off the reaction concentrated by rotary evaporation (41° C., 6 mm Hg) giving a pale yellow oil (18.09 g, 51:1 linear:branched isomer, 90 wt % linear isomer by GC internal standard assay, 16.26 g active, 93%) was washed with toluene (30 mL) to remove non-polar impurities was extracted with toluene (50 mL) The organic layer was washed with water (40 mL) dried over magnesium sulfate filtered concentrated by rotary evaporation giving a pale yellow oil (14.15 g, 34:1 linear:branched isomer, 94 wt % linear isomer by GC internal standard assay, 13.26 g active, 76%)