2-(prop-2-enoylamino)acetic acid

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: 100 g of 25 wt % polyacrylic acid aqueous solution and 2.5 g of N-carboxy methyl acrylamide were polymerized at 60° C. for 3 hours for partial crosslinking. Potassium hydroxide was added to neutralize the pH value to 7.0 and 40 g of T-P400(polymer of triol and propylene oxide, Union Carbide Co., U.S.A.) and 1 g of sodium 2-pyrrolidone-5-carboxylate were added. Deionized water was then added to the resultant product to adjust the solid content thereof to 35 wt %. The viscosity of the resultant solution was measured as 5500 to 6000 cps(30° C.). The resulting product was tested according to the procedures set forth in Example 1, and the test results are listed in Table 1. was measured as 5500 to 6000 cps(30° C.) the test results

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: 100 g of 25 wt % polyacrylic acid aqueous solution (viscosity 8000-12000 cps, 30 ° C.) and 3 g of N-carboxy methyl acrylamide were polymerized at 70° C. for 3 hours for partial crosslinking. Sodium hydroxide was added to neutralize the pH value to 7.0 and 20 g of poly(ether alcohol)(GEP-2800, Dow Chemical Co., U.S.A.) and 1.5 g of sodium 2-pyrrolidone-5-carboxylate were added. Deionized water was then added to the resulting product to adjust the solid content thereof to 35 wt %. The viscosity of the resultant solution was measured as 6000 to 6500 cps(30° C.). The resulting product was tested according to the procedures as set forth in Example 1 and the test results are listed in Table 1. was measured as 6000 to 6500 cps(30° C.) the test results

反应条件: temp:0.01; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: 7.5 g (0.1 mol) mol) glycine was dissolved in 100 ml 2 N NaOH. The solution was cooled to 0° C. and 10.8 g (0.12 mol) acryloyl chloride was added dropwise over 45 minutes, while the temperature was kept below 10° C. The reaction was allowed to continue for one hour at 10° C. The reaction mixture was extracted 2 times with 50 ml tert. butyl methyl ether. The pH was adjusted to pH=3, using a concentrated hydrochloric acid solution and the reaction mixture was saturated with sodium chloride. The mixture was extracted 5 times with 100 ml n.-pentanol. The pooled n.-pentanol fractions were dried over Na2SO4 and evaporated under reduced pressure, after addition of a small fraction BHT as stabilizer. 4.2 g (32.5%) of N-acryloyl-glycine was isolated (m.p. 124-126° C.). N-acryloyl-glycine is Comparative Monomer 5 (see below). was kept below 10° C The reaction mixture was extracted 2 times with 50 ml tert. butyl methyl ether The mixture was extracted 5 times with 100 ml n -pentanol fractions were dried over Na2SO4 evaporated under reduced pressure after addition of a small fraction BHT as stabilizer

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: 100 g of 25 wt % polyacrylic acid aqueous solution and 2.5 g of N-carboxy methyl acrylamide were polymerized at 60° C. for 3 hours for partial crosslinking. Potassium hydroxide was added to neutralize the pH value to 7.0 and 40 g of T-P400(polymer of triol and propylene oxide, Union Carbide Co., U.S.A.) and 1 g of sodium 2-pyrrolidone-5-carboxylate were added. Deionized water was then added to the resultant product to adjust the solid content thereof to 35 wt %. The viscosity of the resultant solution was measured as 5500 to 6000 cps(30° C.). The resulting product was tested according to the procedures set forth in Example 1, and the test results are listed in Table 1. was measured as 5500 to 6000 cps(30° C.) the test results

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: 100 g of 25 wt % polyacrylic acid aqueous solution (viscosity 8000-12000 cps, 30 ° C.) and 3 g of N-carboxy methyl acrylamide were polymerized at 70° C. for 3 hours for partial crosslinking. Sodium hydroxide was added to neutralize the pH value to 7.0 and 20 g of poly(ether alcohol)(GEP-2800, Dow Chemical Co., U.S.A.) and 1.5 g of sodium 2-pyrrolidone-5-carboxylate were added. Deionized water was then added to the resulting product to adjust the solid content thereof to 35 wt %. The viscosity of the resultant solution was measured as 6000 to 6500 cps(30° C.). The resulting product was tested according to the procedures as set forth in Example 1 and the test results are listed in Table 1. was measured as 6000 to 6500 cps(30° C.) the test results

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: 100 g of 25 wt % polyacrylic acid aqueous solution and 2.5 g of N-carboxy methyl acrylamide were polymerized at 60° C. for 3 hours for partial crosslinking. Potassium hydroxide was added to neutralize the pH value to 7.0 and 40 g of T-P400(polymer of triol and propylene oxide, Union Carbide Co., U.S.A.) and 1 g of sodium 2-pyrrolidone-5-carboxylate were added. Deionized water was then added to the resultant product to adjust the solid content thereof to 35 wt %. The viscosity of the resultant solution was measured as 5500 to 6000 cps(30° C.). The resulting product was tested according to the procedures set forth in Example 1, and the test results are listed in Table 1. was measured as 5500 to 6000 cps(30° C.) the test results

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: 100 g of 25 wt % polyacrylic acid aqueous solution (viscosity 8000-12000 cps, 30 ° C.) and 3 g of N-carboxy methyl acrylamide were polymerized at 70° C. for 3 hours for partial crosslinking. Sodium hydroxide was added to neutralize the pH value to 7.0 and 20 g of poly(ether alcohol)(GEP-2800, Dow Chemical Co., U.S.A.) and 1.5 g of sodium 2-pyrrolidone-5-carboxylate were added. Deionized water was then added to the resulting product to adjust the solid content thereof to 35 wt %. The viscosity of the resultant solution was measured as 6000 to 6500 cps(30° C.). The resulting product was tested according to the procedures as set forth in Example 1 and the test results are listed in Table 1. was measured as 6000 to 6500 cps(30° C.) the test results

反应条件: temp:0.01; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: 7.5 g (0.1 mol) mol) glycine was dissolved in 100 ml 2 N NaOH. The solution was cooled to 0° C. and 10.8 g (0.12 mol) acryloyl chloride was added dropwise over 45 minutes, while the temperature was kept below 10° C. The reaction was allowed to continue for one hour at 10° C. The reaction mixture was extracted 2 times with 50 ml tert. butyl methyl ether. The pH was adjusted to pH=3, using a concentrated hydrochloric acid solution and the reaction mixture was saturated with sodium chloride. The mixture was extracted 5 times with 100 ml n.-pentanol. The pooled n.-pentanol fractions were dried over Na2SO4 and evaporated under reduced pressure, after addition of a small fraction BHT as stabilizer. 4.2 g (32.5%) of N-acryloyl-glycine was isolated (m.p. 124-126° C.). N-acryloyl-glycine is Comparative Monomer 5 (see below). was kept below 10° C The reaction mixture was extracted 2 times with 50 ml tert. butyl methyl ether The mixture was extracted 5 times with 100 ml n -pentanol fractions were dried over Na2SO4 evaporated under reduced pressure after addition of a small fraction BHT as stabilizer