正硅酸四乙酯

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: Tetraacetoxysilane was prepared by the reaction of 125 g of silicon tetrachloride and 400 g of acetic acid as blended and stirred at room temperature. When the evolution of hydrogen chloride gas had ceased with precipitation of white crystalline tetraacetoxysilane, the unreacted acetic acid was removed by stripping under a reduced pressure and the residue was dissolved in 300 g of ethyl alcohol. The reaction between the tetraacetoxysilane and ethyl alcohol was carried out by heating the above reaction mixture at 60° C. with agitation for 10 hours. The formation of large amounts of ethyl acetate and hydroxy-containing silane compounds was detected in the resultant reaction mixture which had a solid content of 5.9% by weight upon dilution by adding 120 g of ethyl alcohol. When the evolution of hydrogen chloride gas had ceased with precipitation of white crystalline tetraacetoxysilane the unreacted acetic acid was removed the residue was dissolved in 300 g of ethyl alcohol The reaction between the tetraacetoxysilane and ethyl alcohol by heating the above reaction mixture at 60° C. with agitation for 10 hours reaction mixture which

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: Tetraacetoxysilane was prepared by the reaction of 125 g of silicon tetrachloride and 400 g of acetic acid as blended and stirred at room temperature. When the evolution of hydrogen chloride gas had ceased with precipitation of white crystalline tetraacetoxysilane, the unreacted acetic acid was removed by stripping under a reduced pressure and the residue was dissolved in 300 g of ethyl alcohol. The reaction between the tetraacetoxysilane and ethyl alcohol was carried out by heating the above reaction mixture at 60° C. with agitation for 10 hours. The formation of large amounts of ethyl acetate and hydroxy-containing silane compounds was detected in the resultant reaction mixture which had a solid content of 5.9% by weight upon dilution by adding 120 g of ethyl alcohol. When the evolution of hydrogen chloride gas had ceased with precipitation of white crystalline tetraacetoxysilane the unreacted acetic acid was removed the residue was dissolved in 300 g of ethyl alcohol The reaction between the tetraacetoxysilane and ethyl alcohol by heating the above reaction mixture at 60° C. with agitation for 10 hours reaction mixture which

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: Tetraacetoxysilane was prepared by the reaction of 125 g of silicon tetrachloride and 400 g of acetic acid as blended and stirred at room temperature. When the evolution of hydrogen chloride gas had ceased with precipitation of white crystalline tetraacetoxysilane, the unreacted acetic acid was removed by stripping under a reduced pressure and the residue was dissolved in 300 g of ethyl alcohol. The reaction between the tetraacetoxysilane and ethyl alcohol was carried out by heating the above reaction mixture at 60° C. with agitation for 10 hours. The formation of large amounts of ethyl acetate and hydroxy-containing silane compounds was detected in the resultant reaction mixture which had a solid content of 5.9% by weight upon dilution by adding 120 g of ethyl alcohol. When the evolution of hydrogen chloride gas had ceased with precipitation of white crystalline tetraacetoxysilane the unreacted acetic acid was removed the residue was dissolved in 300 g of ethyl alcohol The reaction between the tetraacetoxysilane and ethyl alcohol by heating the above reaction mixture at 60° C. with agitation for 10 hours reaction mixture which