三丙二醇基甲基乙基醚

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: Tripropylene glycol monomethyl ether (841.6 grams; 3.39 mol), benzoic acid (501.7 grams; 3.46 mol), zinc carbonate 13.5 grams) and toluene (100 ml) were placed into a two liter, three-necked round bottom flask equipped with stirrer, 10" Vigreux column, Dean Stark trap, condenser, heating mantle and thermometer. The reaction temperature was 173° .C at the beginning of the reaction and 235° C. after six hours and 48 minutes. During that time, water (70 ml) was removed. The reaction was continued the next day at 214° C. for an additional three hours and 45 minutes removing additional water (35 ml). Toluene was removed at 65° C. @ 45 mm Hg. The product was washed first with sodium carbonate (170 ml; 15%) at 95°-100° C. for 30 minutes, then with sodium carbonate (22 ml; 15%) and sodium hypochlorite (50 ml), then with sodium carbonate (22 ml; 15%) and sodium hypochlorite (25 ml) with water (300 ml) and finally a second time with water (300 ml). It was dried at 135° C. and filtered to give the desired product (1162.9 grams; 93.6% yield). The product assayed with the following properties: equipped with stirrer 10" Vigreux column, Dean Stark trap, condenser, heating mantle was 173° at the beginning of the reaction and 235° C. after six hours 48 minutes During that time, water (70 ml) was removed at 214° C. for an additional three hours 45 minutes removing additional water (35 ml) Toluene was removed at 65° C. @ 45 mm Hg The product was washed first with sodium carbonate (170 ml; 15%) at 95°-100° C. for 30 minutes It was dried at 135° C. filtered

反应条件: temp:60.01; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: Then, 207.6 g (2.0 mols) of trimethyl borate was added to 618 g (3.0 mols) of tripropylene glycol monomethyl ether. The mixture was heated to 60° C. with stirring in a dry nitrogen atmosphere. After the mixture was kept at 60° C. for 1 hour, it was heated to 120° C. over a period of 1 hour. After the temperature reached 120° C., the pressure in the system was gradually reduced. The system was kept at a pressure of 2.67 kPa (20 mmHg) or lower for 3 hours to remove volatile matters produced with progress of ester interchange reaction of boric acid and excess trimethyl borate, followed by filtration to obtain 610 g of a polymerizable boron-containing compound G (an esterification product of boric acid with tripropylene glycol monomethyl ether) represented by the formula (3). An infrared absorption spectrum of the resulting polymerizable boron-containing compound G was measured to confirm that the absorption band originating from hydroxyl group at 3300 cm−1 disappeared. it was heated to 120° C. over a period of 1 hour reached 120° C. The system was kept at a pressure of 2.67 kPa (20 mmHg) or lower for 3 hours to remove volatile matters

反应条件: temp:75.01; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: 207.6 Grams (2.0 mols) of trimethyl borate was added to 202 g (1.0 mol) of dipropylene glycol monomethacrylate and 412 g (2.0 mols) of tripropylene glycol monomethyl ether, followed by keeping them at 60° C. for 1 hour with stirring in a dry air atmosphere and then heating to 75° C. After the temperature reached 75° C., the pressure in the system was gradually reduced. The system was kept at a pressure of 2.67 kPa (20 mmHg) or lower for 6 hours to remove volatile matters produced with progress of ester interchange reaction of boric acid and excess trimethyl borate, followed by filtration to obtain 610 g of the polymerizable boron-containing compound B represented by the formula (1). An infrared absorption spectrum of the resulting polymerizable boron-containing compound B was measured to confirm that the absorption band originating from hydroxyl group at 3300 cm−1 disappeared. at 60° C. for 1 hour reached 75° C. to remove volatile matters