乙酸镁 四水合物

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: An aqueous magnesium acetate solution was prepared by adding 1.07 g of magnesium acetate tetrahydrate as a Group 2 or 3 element compound to 30 g of ion-exchanged water and then stirring this solution with a homomixer T. K. ROBOMIX (manufactured by PRIMIX Corporation). Then, 0.44 g of 3-aminopropyltriethoxysilane (KBE-903 manufactured by Shin-Etsu Chemical Co., Ltd.) as a silane coupling agent was gradually added to the aqueous solution. This mixture was subsequently stirred for 5 hours to induce hydrolysis and a condensation reaction of the silane coupling agent, thereby producing a suspension containing a composite compound which contained magnesium and silicon. This mixture was subsequently stirred for 5 hours hydrolysis producing a suspension containing a composite compound which

反应条件: temp:40.01; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: A glass flask was equipped with a thermometer, mechanical paddle stirrer and a water cooled condenser. Crushed maleic anhydride (1.92 parts) was added to a solution of 1 part m-phenylenediamine and 13 parts acetone over a 15-minute period. The heterogeneous reaction mixture was stirred at 40° C. for 1 hour. Acetic anhydride (2.44 parts), 0.32 part triethylamine, and 0.04 part magnesium acetate tetrahydrate were added all at once. The temperature was raised to 60° C. using a heating mantle and maintained for 4 hours. The reaction mixture was cooled, 20 parts water added, and the precipitated product isolated by filtration using a vacuum filter funnel. The filter cake was washed with water and dried for 24 hours at 60°-70° C. in a vacuum oven. A 74% yield of N,N'-m-phenylenedimaleimide, m.p. 203°-204° C. was obtained. A glass flask was equipped with a thermometer, mechanical paddle stirrer and a water cooled condenser The temperature was raised to 60° C. maintained for 4 hours The reaction mixture was cooled the precipitated product isolated by filtration filter funnel The filter cake was washed with water dried for 24 hours at 60°-70° C. in a vacuum oven

反应条件: temp:40.01; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: A glass flask was equipped with a thermometer, mechanical paddle stirrer and a water cooled condenser. Crushed maleic anhydride (1.92 parts) was added to a solution of 1 part m-phenylenediamine and 13 parts acetone over a 15-minute period. The heterogeneous reaction mixture was stirred at 40° C. for 1 hour. Acetic anhydride (2.44 parts), 0.32 part triethylamine, and 0.04 part magnesium acetate tetrahydrate were added all at once. The temperature was raised to 60° C. using a heating mantle and maintained for 4 hours. The reaction mixture was cooled, 20 parts water added, and the precipitated product isolated by filtration using a vacuum filter funnel. The filter cake was washed with water and dried for 24 hours at 60°-70° C. in a vacuum oven. A 74% yield of N,N'-m-phenylenedimaleimide, m.p. 203°-204° C. was obtained. A glass flask was equipped with a thermometer, mechanical paddle stirrer and a water cooled condenser The temperature was raised to 60° C. maintained for 4 hours The reaction mixture was cooled the precipitated product isolated by filtration filter funnel The filter cake was washed with water dried for 24 hours at 60°-70° C. in a vacuum oven

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: An aqueous magnesium acetate solution was prepared by adding 1.07 g of magnesium acetate tetrahydrate as a Group 2 or 3 element compound to 30 g of ion-exchanged water and then stirring this solution with a homomixer T. K. ROBOMIX (manufactured by PRIMIX Corporation). Then, 0.44 g of 3-aminopropyltriethoxysilane (KBE-903 manufactured by Shin-Etsu Chemical Co., Ltd.) as a silane coupling agent was gradually added to the aqueous solution. This mixture was subsequently stirred for 5 hours to induce hydrolysis and a condensation reaction of the silane coupling agent, thereby producing a suspension containing a composite compound which contained magnesium and silicon. This mixture was subsequently stirred for 5 hours hydrolysis producing a suspension containing a composite compound which

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: An aqueous magnesium acetate solution was prepared by adding 1.07 g of magnesium acetate tetrahydrate as a Group 2 or 3 element compound to 30 g of ion-exchanged water and then stirring this solution with a homomixer T. K. ROBOMIX (manufactured by PRIMIX Corporation). Then, 0.44 g of 3-aminopropyltriethoxysilane (KBE-903 manufactured by Shin-Etsu Chemical Co., Ltd.) as a silane coupling agent was gradually added to the aqueous solution. This mixture was subsequently stirred for 5 hours to induce hydrolysis and a condensation reaction of the silane coupling agent, thereby producing a suspension containing a composite compound which contained magnesium and silicon. This mixture was subsequently stirred for 5 hours hydrolysis producing a suspension containing a composite compound which

反应条件: temp:40.01; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: A glass flask was equipped with a thermometer, mechanical paddle stirrer and a water cooled condenser. Crushed maleic anhydride (1.92 parts) was added to a solution of 1 part m-phenylenediamine and 13 parts acetone over a 15-minute period. The heterogeneous reaction mixture was stirred at 40° C. for 1 hour. Acetic anhydride (2.44 parts), 0.32 part triethylamine, and 0.04 part magnesium acetate tetrahydrate were added all at once. The temperature was raised to 60° C. using a heating mantle and maintained for 4 hours. The reaction mixture was cooled, 20 parts water added, and the precipitated product isolated by filtration using a vacuum filter funnel. The filter cake was washed with water and dried for 24 hours at 60°-70° C. in a vacuum oven. A 74% yield of N,N'-m-phenylenedimaleimide, m.p. 203°-204° C. was obtained. A glass flask was equipped with a thermometer, mechanical paddle stirrer and a water cooled condenser The temperature was raised to 60° C. maintained for 4 hours The reaction mixture was cooled the precipitated product isolated by filtration filter funnel The filter cake was washed with water dried for 24 hours at 60°-70° C. in a vacuum oven

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: Into a 300 ml. flask equipped as in EXAMPLE I and maintained under a nitrogen atmosphere were added 21.5 grams magnesium acetate tetrahydrate and 80 ml. acetic anhydride and the mixture was heated at the reflux temperature for 1 hour. After cooling, a clear liquid was drawn off and the remaining solid was dried at 35° C. under a vacuum of 0.3 mm mercury for several hours to obtain anhydrous magnesium acetate. flask equipped as in EXAMPLE I maintained under a nitrogen atmosphere After cooling the remaining solid was dried at 35° C. under a vacuum of 0.3 mm mercury for several hours

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: Into a 300 ml. flask equipped with mechanical stirrer and a condenser, and maintained under a nitrogen atmosphere, were added 21.5 grams magnesium acetate tetrahydrate and 100 ml. acetic anhydride and the mixture was heated at the reflux temperature for 3 hours. After the mixture had cooled, the liquid was drawn off and the solid dried at 40° C. under a vacuum of 0.2 mm mercury for several hours to obtain anhydrous magnesium acetate. flask equipped with mechanical stirrer and a condenser maintained under a nitrogen atmosphere After the mixture had cooled the solid dried at 40° C. under a vacuum of 0.2 mm mercury for several hours

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: Into a 300 ml. flask equipped as in EXAMPLE I and maintained under a nitrogen atmosphere were added 21.5 grams magnesium acetate tetrahydrate and 80 ml. acetic anhydride and the mixture was heated at the reflux temperature for 1 hour. After cooling, a clear liquid was drawn off and the remaining solid was dried at 35° C. under a vacuum of 0.3 mm mercury for several hours to obtain anhydrous magnesium acetate. flask equipped as in EXAMPLE I maintained under a nitrogen atmosphere After cooling the remaining solid was dried at 35° C. under a vacuum of 0.3 mm mercury for several hours

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: Into a 300 ml. flask equipped with mechanical stirrer and a condenser, and maintained under a nitrogen atmosphere, were added 21.5 grams magnesium acetate tetrahydrate and 100 ml. acetic anhydride and the mixture was heated at the reflux temperature for 3 hours. After the mixture had cooled, the liquid was drawn off and the solid dried at 40° C. under a vacuum of 0.2 mm mercury for several hours to obtain anhydrous magnesium acetate. flask equipped with mechanical stirrer and a condenser maintained under a nitrogen atmosphere After the mixture had cooled the solid dried at 40° C. under a vacuum of 0.2 mm mercury for several hours

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: Magnesium acetate tetrahydrate (4.28 g) is added to 200 grams of deionized water. The pH of the resulting solution is 8.02.

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: First, 60 g of hydrated alumina (trade name: Disperal HP14 available from Sasol Ltd.) was added to 800 g of pure water, and 1.29 g of magnesium acetate tetrahydrate (element content of Mg/element content of Al=0.006) was added to the resultant mixture. The resultant dispersoid was dried by a spray-drying method to obtain hydrated alumina 1 which magnesium acetate adhered to. The drying temperature (gas phase temperature) was 170° C. The acid site strength of the hydrated alumina 1 was measured by temperature-programmed desorption (TPD) that determines surface activity using ammonia gas. As a result, the presence of acid sites was not confirmed, and it was found that magnesium acetate adhered to hydrated alumina. The resultant dispersoid was dried by a spray-drying method