四甲基二乙氧基二硅烷

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: In the same manner as in Example 1, change of the average molecular weight of the resulting polysilanes was examined by changing the amount of methyl lithium to be used as a reaction starting compound. The results including those of Example 1 and the yields and properties of the products are shown in Table 1. In Example 4, after the disilane compound and methyl lithium were reacted, the reaction mixture was applied to gas chromatography before heating to confirm that 1,1,2-trimethyl-1,2,2-triethoxydisilane and 1,1,2,2-tetramethyl-1,2-diethoxydisilane were produced. From the reaction mixture of Example 4, no solid was obtained by reprecipitation so that low boiling point compounds were removed under conditions of 180° C. and 1 Torr to give a final product. the yields before heating