反应条件: temp:145.01; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: A reactor of the kind described in Example 8 is charged with 240.4 g (1.0 mol) of perhydrobisphenol A, 3.14 g (0.02 mol) of powdered tin difluoride and 5.28 g (0.02 mol) of 18-crown-6, and the charge is heated to 145° C., whereupon the educt melts. Then, with efficient stirring 152.12 ml (1.94 mol) of epichlorohydrin are added over 30 minutes. The reaction is allowed to continue for 12 hours, then cooled to 55° C., 250 ml of toluene are added and, then, at this temperature, 155.2 g (1.94 mol) of a 50% aqueous solution of sodium hydroxide are added dropwise with efficient stirring over 30 minutes. After stirring for 4.5 hours at 55°-60° C. and cooling to room temperature, the suspension is filtered and the filtrate is washed with toluene. The phases are separated, and the aqueous phase is extracted with 2×100 ml of ethyl acetate. The combined organic phases are washed with a small an amount of 10% KH2PO4 solution as possible and then with water until neutral, dried over magnesium sulfate and filtered. The filtrate is freed from solvent on a rotary evaporator under vacuum (bath temperature 70° C.). Yield: 330.8 g (94% of theory) of yellowish perhydrobisphenol A diglycidyl ether for which the following analytical values are obtained: epoxy value: 4.31 eq/kg (76% of theory); total chlorine content: 2.1%; hydrolysable chlorine content: 171 ppm. A reactor of the kind described in Example 8 are added over 30 minutes cooled to 55° C. After stirring for 4.5 hours at 55°-60° C. cooling to room temperature the suspension is filtered the filtrate is washed with toluene The phases are separated the aqueous phase is extracted with 2×100 ml of ethyl acetate The combined organic phases are washed with a small an amount of 10% KH2PO4 solution as possible and then with water until neutral, dried over magnesium sulfate filtered The filtrate is freed from solvent on a rotary evaporator under vacuum (bath temperature 70° C.)

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: Diglycidyl ether resin (technical product) manufactured by condensation of hydrogenated diomethane (2,2-bis-(p-hydroxycyclohexyl)-propane) with a stoichiometric excess of epichlorohydrin in the presence of alkali, consisting mainly of hydrogenated diomethane-diglycidal ether of the formula ##EQU5## which is liquid at room temperature and has an epoxide content of 4.46 epoxide equivalents/kg. at room temperature

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: The process described in Japanese Patent Laid-Open Publication No. 59742/1992, however, has a problem of using expensive alicyclic diol. If 2,2-bis(4-hydroxyphenyl)propane that is relatively inexpensive is used as a starting material, reactions of two steps, namely, hydrogenation reaction of 2,2-bis(4-hydroxyphenyl)propane and oxidation reaction of 2,2-bis(4-hydroxycyclohexyl)propane obtained by the hydrogenation reaction, must be conducted to produce 2,2-bis(4-oxocyclohexyl)propane, so that the process becomes complicated. obtained by the hydrogenation reaction

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: The process described in Japanese Patent Laid-Open Publication No. 59742/1992, however, has a problem of using expensive alicyclic diol. If 2,2-bis(4-hydroxyphenyl)propane that is relatively inexpensive is used as a starting material, reactions of two steps, namely, hydrogenation reaction of 2,2-bis(4-hydroxyphenyl)propane and oxidation reaction of 2,2-bis(4-hydroxycyclohexyl)propane obtained by the hydrogenation reaction, must be conducted to produce 2,2-bis(4-oxocyclohexyl)propane, so that the process becomes complicated. obtained by the hydrogenation reaction

反应条件: temp:145.01; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: A reactor of the kind described in Example 8 is charged with 240.4 g (1.0 mol) of perhydrobisphenol A, 3.14 g (0.02 mol) of powdered tin difluoride and 5.28 g (0.02 mol) of 18-crown-6, and the charge is heated to 145° C., whereupon the educt melts. Then, with efficient stirring 152.12 ml (1.94 mol) of epichlorohydrin are added over 30 minutes. The reaction is allowed to continue for 12 hours, then cooled to 55° C., 250 ml of toluene are added and, then, at this temperature, 155.2 g (1.94 mol) of a 50% aqueous solution of sodium hydroxide are added dropwise with efficient stirring over 30 minutes. After stirring for 4.5 hours at 55°-60° C. and cooling to room temperature, the suspension is filtered and the filtrate is washed with toluene. The phases are separated, and the aqueous phase is extracted with 2×100 ml of ethyl acetate. The combined organic phases are washed with a small an amount of 10% KH2PO4 solution as possible and then with water until neutral, dried over magnesium sulfate and filtered. The filtrate is freed from solvent on a rotary evaporator under vacuum (bath temperature 70° C.). Yield: 330.8 g (94% of theory) of yellowish perhydrobisphenol A diglycidyl ether for which the following analytical values are obtained: epoxy value: 4.31 eq/kg (76% of theory); total chlorine content: 2.1%; hydrolysable chlorine content: 171 ppm. A reactor of the kind described in Example 8 are added over 30 minutes cooled to 55° C. After stirring for 4.5 hours at 55°-60° C. cooling to room temperature the suspension is filtered the filtrate is washed with toluene The phases are separated the aqueous phase is extracted with 2×100 ml of ethyl acetate The combined organic phases are washed with a small an amount of 10% KH2PO4 solution as possible and then with water until neutral, dried over magnesium sulfate filtered The filtrate is freed from solvent on a rotary evaporator under vacuum (bath temperature 70° C.)

反应条件: temp:145.01; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: A reactor of the kind described in Example 8 is charged with 240.4 g (1.0 mol) of perhydrobisphenol A, 3.14 g (0.02 mol) of powdered tin difluoride and 5.28 g (0.02 mol) of 18-crown-6, and the charge is heated to 145° C., whereupon the educt melts. Then, with efficient stirring 152.12 ml (1.94 mol) of epichlorohydrin are added over 30 minutes. The reaction is allowed to continue for 12 hours, then cooled to 55° C., 250 ml of toluene are added and, then, at this temperature, 155.2 g (1.94 mol) of a 50% aqueous solution of sodium hydroxide are added dropwise with efficient stirring over 30 minutes. After stirring for 4.5 hours at 55°-60° C. and cooling to room temperature, the suspension is filtered and the filtrate is washed with toluene. The phases are separated, and the aqueous phase is extracted with 2×100 ml of ethyl acetate. The combined organic phases are washed with a small an amount of 10% KH2PO4 solution as possible and then with water until neutral, dried over magnesium sulfate and filtered. The filtrate is freed from solvent on a rotary evaporator under vacuum (bath temperature 70° C.). Yield: 330.8 g (94% of theory) of yellowish perhydrobisphenol A diglycidyl ether for which the following analytical values are obtained: epoxy value: 4.31 eq/kg (76% of theory); total chlorine content: 2.1%; hydrolysable chlorine content: 171 ppm. A reactor of the kind described in Example 8 are added over 30 minutes cooled to 55° C. After stirring for 4.5 hours at 55°-60° C. cooling to room temperature the suspension is filtered the filtrate is washed with toluene The phases are separated the aqueous phase is extracted with 2×100 ml of ethyl acetate The combined organic phases are washed with a small an amount of 10% KH2PO4 solution as possible and then with water until neutral, dried over magnesium sulfate filtered The filtrate is freed from solvent on a rotary evaporator under vacuum (bath temperature 70° C.)

反应条件: temp:120.01; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: Into a reaction vessel equipped as in Example A was charged 1064 grams tetramethoxymethyl glycoluril (TMMGU) and 532 grams hydrogenated bisphenol-A which was melted and heated to 120° C. 14 grams of Polycat 200 catayst was added slowly over a 30-minute period at 110°-120° C. to control foaming. The batch temperature was then raised slowly to 160° C. and foaming controlled with 2 grams additions of Quadrol. Total Quadrol added is 10.4 grams. Upon reaching a tack temperature of 80°-85° C., the batch was discharged into a tray. The product, a methoxy-methyl-functional copolymer of TMMGU and HBPA, has a tack temperature of 84° C., a viscosity at 50% non-volatile content in meta-pyrol of K and a methoxy equivalent weight of 212. A small amount of self-condensation had also occurred in this reaction in addition to the primary methoxyhydroxyl reaction. Into a reaction vessel equipped as in Example A The batch temperature was then raised slowly to 160° C. a tack temperature of 80°-85° C. a tack temperature of 84° C. A small amount of self-condensation

反应条件: temp:120.01; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: Into a reaction vessel equipped as in Example A was charged 1064 grams tetramethoxymethyl glycoluril (TMMGU) and 532 grams hydrogenated bisphenol-A which was melted and heated to 120° C. 14 grams of Polycat 200 catayst was added slowly over a 30-minute period at 110°-120° C. to control foaming. The batch temperature was then raised slowly to 160° C. and foaming controlled with 2 grams additions of Quadrol. Total Quadrol added is 10.4 grams. Upon reaching a tack temperature of 80°-85° C., the batch was discharged into a tray. The product, a methoxy-methyl-functional copolymer of TMMGU and HBPA, has a tack temperature of 84° C., a viscosity at 50% non-volatile content in meta-pyrol of K and a methoxy equivalent weight of 212. A small amount of self-condensation had also occurred in this reaction in addition to the primary methoxyhydroxyl reaction. Into a reaction vessel equipped as in Example A The batch temperature was then raised slowly to 160° C. a tack temperature of 80°-85° C. a tack temperature of 84° C. A small amount of self-condensation

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: Diglycidyl ether resin (technical product) manufactured by condensation of hydrogenated diomethane (2,2-bis-(p-hydroxycyclohexyl)-propane) with a stoichiometric excess of epichlorohydrin in the presence of alkali, consisting mainly of hydrogenated diomethane-diglycidal ether of the formula ##EQU5## which is liquid at room temperature and has an epoxide content of 4.46 epoxide equivalents/kg. at room temperature

反应条件: temp:0.00; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: The process described in Japanese Patent Laid-Open Publication No. 59742/1992, however, has a problem of using expensive alicyclic diol. If 2,2-bis(4-hydroxyphenyl)propane that is relatively inexpensive is used as a starting material, reactions of two steps, namely, hydrogenation reaction of 2,2-bis(4-hydroxyphenyl)propane and oxidation reaction of 2,2-bis(4-hydroxycyclohexyl)propane obtained by the hydrogenation reaction, must be conducted to produce 2,2-bis(4-oxocyclohexyl)propane, so that the process becomes complicated. obtained by the hydrogenation reaction

反应条件: temp:145.01; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: A reactor of the kind described in Example 8 is charged with 240.4 g (1.0 mol) of perhydrobisphenol A, 3.14 g (0.02 mol) of powdered tin difluoride and 5.28 g (0.02 mol) of 18-crown-6, and the charge is heated to 145° C., whereupon the educt melts. Then, with efficient stirring 152.12 ml (1.94 mol) of epichlorohydrin are added over 30 minutes. The reaction is allowed to continue for 12 hours, then cooled to 55° C., 250 ml of toluene are added and, then, at this temperature, 155.2 g (1.94 mol) of a 50% aqueous solution of sodium hydroxide are added dropwise with efficient stirring over 30 minutes. After stirring for 4.5 hours at 55°-60° C. and cooling to room temperature, the suspension is filtered and the filtrate is washed with toluene. The phases are separated, and the aqueous phase is extracted with 2×100 ml of ethyl acetate. The combined organic phases are washed with a small an amount of 10% KH2PO4 solution as possible and then with water until neutral, dried over magnesium sulfate and filtered. The filtrate is freed from solvent on a rotary evaporator under vacuum (bath temperature 70° C.). Yield: 330.8 g (94% of theory) of yellowish perhydrobisphenol A diglycidyl ether for which the following analytical values are obtained: epoxy value: 4.31 eq/kg (76% of theory); total chlorine content: 2.1%; hydrolysable chlorine content: 171 ppm. A reactor of the kind described in Example 8 are added over 30 minutes cooled to 55° C. After stirring for 4.5 hours at 55°-60° C. cooling to room temperature the suspension is filtered the filtrate is washed with toluene The phases are separated the aqueous phase is extracted with 2×100 ml of ethyl acetate The combined organic phases are washed with a small an amount of 10% KH2PO4 solution as possible and then with water until neutral, dried over magnesium sulfate filtered The filtrate is freed from solvent on a rotary evaporator under vacuum (bath temperature 70° C.)

反应条件: temp:120.01; pressure:0.00; stir:; See reaction.notes.procedure_details.

实验步骤: Into a reaction vessel equipped as in Example A was charged 1064 grams tetramethoxymethyl glycoluril (TMMGU) and 532 grams hydrogenated bisphenol-A which was melted and heated to 120° C. 14 grams of Polycat 200 catayst was added slowly over a 30-minute period at 110°-120° C. to control foaming. The batch temperature was then raised slowly to 160° C. and foaming controlled with 2 grams additions of Quadrol. Total Quadrol added is 10.4 grams. Upon reaching a tack temperature of 80°-85° C., the batch was discharged into a tray. The product, a methoxy-methyl-functional copolymer of TMMGU and HBPA, has a tack temperature of 84° C., a viscosity at 50% non-volatile content in meta-pyrol of K and a methoxy equivalent weight of 212. A small amount of self-condensation had also occurred in this reaction in addition to the primary methoxyhydroxyl reaction. Into a reaction vessel equipped as in Example A The batch temperature was then raised slowly to 160° C. a tack temperature of 80°-85° C. a tack temperature of 84° C. A small amount of self-condensation